3J01 garyndysy Fe-Ni-Cr austenit ýagyşy bilen güýçlendirilen ýokary elastik garyndydyr. Gaty ergin bejergisinden soň, oňat plastisitliligi, pes gatylygy we aňsat gaýtadan işlenmegi we emele gelmegi bolýar. Gaty ergin ýa-da sowuk dartyş garramagyndan soň ýokary mehaniki we elastik häsiýetler alyndy.
Garyndy | C | Mn | Si | P | S | Ni | Cr | Ti | Al | Fe |
3J01 | ≤0.05 | .001.00 | ≤0.80 | ≤0.020 | ≤0.020 | 34.5-36.5 | 11.5-13.0 | 2.70-3.20 | 1.00-1.80 | Gadagan etmek |
Dykyzlygy (g / cm3) | Çydamlylyk(L2 - m) | Wikers gatylyk (HV) | Çeýeligiň moduly(E / MPa) | Gyrkygyň deformasiýasy(G / MPa) | Magnit ýygylygy(K / 106) |
8.0 | 1.02 | 400-480 | 186500-206000 | 68500-78500 | 150-250 |
.Agdaý | Galyňlygy / diametri (mm) | Dartyş güýjiσb / MPa | Uzalma % Asaly |
annealing | 0.20 ~ 0.50 | ≤981 | ≥20 |
Sowuk çekildi | 0.20 ~ 3.0 | ≥981 | - |
3J01 garyndysy ýokary güýç, ýokary elastik modul, ownuk elastik täsir we histerez, gowşak magnit, gowy poslama garşylyk we termiki durnuklylyk aýratynlyklaryna eýedir we has ýokary temperaturada, has uly stresde ýa-da poslaýjy media şertlerinde işläp biler.
Azot kislotasyna ýa-da film gutulary, diafragmalar, gabyklar, geçiriji çybyklar, päsgelçilikler we beýleki elastik gurluşlar ýaly her dürli awiasiýa elastik duýgur elementleri we azot kislotasyna çydamly bölekleri öndürmek üçin ulanylýar.